Protein Release from Biodegradable Poly(ε-caprolactone)-Chitosan Scaffolds Prepared in scCO2

Gregor Kravanja, Maja Globočnik, Mateja Primožič, Željko Knez, Maja Leitgeb

Abstract


To study the release patterns of protein bovine serum albumin (BSA), porous poly(ε-caprolactone)-chitosan scaffolds with entrapped BSA were fabricated by using supercritical CO2 (scCO2) for its potential use in tissue engineering applications. An emulsion, consisting of a polymer-solvent solution and buffer protein solution was saturated with scCO2 at 12 MPa and 37 °C and then rapidly depressurized through a release valve causing bubble nucleation and precipitation of the composite material. The controlled total protein release from biodegradable poly(ε-caprolactone) with 5% chitosan (w/w) scaffolds was assessed by Bradford protein assay. After 16 to 20 days of protein release testing, 58.8% of the protein was released from composite with PCL (Mw=10,000 g/mol) and 43.9% from composite with PCL (Mw=60,000 g/mol). Preliminary studies for characterization of the prepared composite biomaterials using FTIR spectra, ESEM photo analysis and DSC analysis have been carried out.


Keywords


Protein release; PCL polymer; chitosan; scaffold; supercritical CO2

Full Text:

PDF


DOI: http://dx.doi.org/10.17344/acsi.2018.4822

Refbacks

  • There are currently no refbacks.


Copyright (c) 2017 Gregor Kravanja, Maja Globočnik, Mateja Primožič, Željko Knez, Maja Leitgeb

Creative Commons License
This work is licensed under a Creative Commons Attribution 4.0 International License.